Mosca GmbH
INT

Strapping strap

PET are particularly tear-resistant and elastic at the same time. As a result, they reliably absorb shocks during transportation and are equally suitable for welding using friction welding or ultrasound. They are also relatively easy to recycle after use.

35 Strapping bands

PET 95054

Bandwidth

9.5 mm

Thickness

0.54 mm

Average breaking load

185 kg

Core Ø

406 mm

PET 95060

Bandwidth

9.5 mm

Thickness

0.60 mm

Average breaking load

220 kg

Core Ø

406 mm

PET 95064

Bandwidth

9.5 mm

Thickness

0.64 mm

Average breaking load

220 kg

Core Ø

406 mm

PET 108039

Bandwidth

10.8 mm

Thickness

0.39 mm

Average breaking load

135 kg

Core Ø

200 mm

PET 110053

Bandwidth

11.0 mm

Thickness

0.53 mm

Average breaking load

210 kg

Core Ø

406 mm

PET 120050

Bandwidth

12.0 mm

Thickness

0.50 mm

Average breaking load

210 kg

Core Ø

406 mm

PET 120054

Bandwidth

12.0 mm

Thickness

0.54 mm

Average breaking load

235 kg

Core Ø

406 mm

PET 120058

Bandwidth

12.0 mm

Thickness

0.58 mm

Average breaking load

225 kg

Core Ø

406 mm

PET 120060

Bandwidth

12.0 mm

Thickness

0.60 mm

Average breaking load

260 kg

Core Ø

406 mm

PET 120062

Bandwidth

12.0 mm

Thickness

0.62 mm

Average breaking load

265 kg

Core Ø

406 mm

PET 120066

Bandwidth

12.0 mm

Thickness

0.66 mm

Average breaking load

270 kg

Core Ø

406 mm

PET 120070

Bandwidth

12.0 mm

Thickness

0.70 mm

Average breaking load

325 kg

Core Ø

406 mm

PET 120080

Bandwidth

12.0 mm

Thickness

0.80 mm

Average breaking load

370 kg

Core Ø

406 mm

PET 120083

Bandwidth

12.0 mm

Thickness

0.83 mm

Average breaking load

395 kg

Core Ø

406 mm

PET 120088

Bandwidth

12.0 mm

Thickness

0.88 mm

Average breaking load

420 kg

Core Ø

406 mm